CMOS fabrication

ABSTRACT

A method of manufacturing a memory device includes an nMOS region and a pMOS region in a substrate. A first gate is defined within the nMOS region, and a second gate is defined in the pMOS region. Disposable spacers are simultaneously defined about the first and second gates. The nMOS and pMOS regions are selectively masked, one at a time, and LDD and Halo implants performed using the same masks as the source/drain implants for each region, by etching back spacers between source/drain implant and LDD/Halo implants. All transistor doping steps, including enhancement, gate and well doping, can be performed using a single mask for each of the nMOS and pMOS regions. Channel length can also be tailored by trimming spacers in one of the regions prior to source/drain doping.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The invention relates generally to integrated circuit design and, more particularly, to a process for defining complementary metal oxide semiconductor (“CMOS”) transistors.

2. Description of the Related Art

Integrated circuits are typically produced according to a series of complex fabrication steps including deposition, masking, etching and doping steps. The complexity of the fabrication greatly increases the cost of the integrated circuits, and often results in relatively low manufacturing efficiency.

For example, for memory circuits or devices, such as dynamic random access memories (DRAMs), static random access memories (SRAMs) and ferroelectric (FE) memories, the fabrication of the CMOS logic around the periphery traditionally comprises a number of relatively time-consuming and expensive masking steps.

First, a mask is used to define the active areas of the transistors in the CMOS by shallow trench isolation (STI). According to some manufacturing methods, this same masking stage may be used to simultaneously define active areas in the array by STI. Next, a gate oxide is defined, typically in both the periphery and array. Using one mask for the n-channel metal oxide semiconductors (nMOS) and another mask for the p-channel metal oxide semiconductors (pMOS), the well, n-channel enhancement implants and polysilicon workfunction implants are defined in the next step.

The polysilicon for forming the gates in the CMOS may then be formed using another mask. The lightly doped drain (LDD) implant and Halo implant (or pocket implant, as it is sometimes referred to) may then be formed around the CMOS gates using one mask for the nMOS, one mask for the pMOS, and yet another mask for the array.

Spacers are then typically formed along the vertical sidewalls of gate electrodes of both the periphery and array. The source and drain regions for the transistors may then be doped using a mask for each of the nMOS and pMOS regions. Finally, a low k gap fill oxide is deposited along the top of the memory device, and the device undergoes rapid thermal processing (RTP) for dopant activation. The transistors and other circuit elements of the array and periphery are thereby defined, and lines may then be connected thereto according to other steps well known to those of skill in the art.

As is clear from the description above, a typical CMOS fabrication process necessitates the use of many masks, and is a complex, time-consuming process. An exemplary CMOS fabrication process flow as described above, for example, employs eight (8) masks from definition of field isolation until transistor source/drain doping for each of the nMOS and pMOS regions. There is a need, therefore, for a less complex manufacturing technique that would use fewer masks, and that would also have an improved yield in comparison to traditional techniques.

SUMMARY OF THE INVENTION

According to one aspect of the invention, a process is provided for forming a memory device. The method includes patterning gates in nMOS and pMOS regions for CMOS circuits. The pMOS regions are masked with a first mask. Source/drain doping and supplemental doping between source/drain regions and the gates are conducted in the nMOS regions while the pMOS regions remain masked with the first mask. The nMOS regions are masked with a second mask. Source/drain doping and supplemental doping between source drain regions and the gates are conducted in the pMOS regions while the nMOS regions remain masked with the second mask. Exemplary supplemental doping includes lightly doped drain (LDD) and pocket or Halo implants.

According to another aspect of the invention, a method of manufacturing a memory device is disclosed. The method includes providing a substrate and defining a pMOS region and an nMOS region in the substrate. A first gate is defined in the nMOS region, and a second gate is defined in the pMOS region. First and second spacers are formed over the first and second gates, respectively. The nMOS and pMOS regions are selectively masked, and at least a portion of the first spacers is etched back from the first gate while the pMOS region is masked.

According to another aspect of the invention, a method is provided for manufacturing a memory device. The method includes providing a substrate and defining at least two active areas within the substrate, where at least one of said active areas comprises an nMOS region, and at least another of said active areas comprising a pMOS region. A first gate is patterned within the nMOS region and a second gate is patterned within the pMOS region. First disposable spacers are formed on the first gate and second disposable spacers are simultaneously formed on the second gate. The first disposable spacers are trimmed to be smaller than a width of the second disposable spacer.

According to another aspect of the invention, a method of fabricating CMOS circuits includes defining field isolation, patterning CMOS gates and conducting complete CMOS transistor doping using six or fewer masks.

According to another aspect of the invention, an integrated circuit is provided. The integrated circuit comprises a substrate, an nMOS gate over an n-channel in the substrate, and a pMOS gate over a p-channel in the substrate. The nMOS and pMOS gates have approximately the same widths while the n-channel is shorter than the pMOS channel.

According to another embodiment of the invention, a system comprising a CMOS circuit is provided. The CMOS circuit comprises a substrate and a CMOS transistor gate formed integrally with the substrate. Source/drain regions are formed within the substrate near the gate, and lightly doped drain (LDD) regions are formed at least partially between the source/drain regions and the gate. A gap-fill oxide, with a dielectric constant of less than about 3.5 directly contacts sidewalls of the gate.

BRIEF DESCRIPTION OF THE DRAWINGS

These and other aspects of the invention will be better understood from the detailed description of the preferred embodiments and from the appended drawings, which are meant to illustrate and not to limit the invention, and in which:

FIG. 1 is a flow chart illustrating one process for fabricating CMOS circuits according to a preferred embodiment of the present invention.

FIG. 2 illustrates a cross-sectional view of a portion of a memory device within which nMOS and pMOS transistors may be formed according to a preferred embodiment of the present invention.

FIG. 3 illustrates a cross-sectional view of the device of FIG. 2 after a mask step, optional spacer trim in n-channel areas, n+ implant and n-channel enhancements implant.

FIG. 4 illustrates a cross-sectional view of the device of FIG. 3 after spacer removal in n-channel areas, LDD implant and Halo implant.

FIG. 5 illustrates a schematic cross-sectional view of the nMOS region of the device of FIG. 4 after LDD implant and Halo implant.

FIG. 6 illustrates a cross-sectional view of the device of FIG. 4 after a second mask step, optional spacer trim in p-channel areas, p+ implant and p-channel enhancements implant.

FIG. 7 illustrates a cross-sectional view of the device of FIG. 6 after spacer removal in p-channel areas, LDD implant and Halo implant.

FIG. 8 illustrates a cross-sectional view of the device of FIG. 7 after mask removal, low k gap-fill oxide and RTP.

FIG. 9 illustrates a schematic cross-sectional view of the nMOS region of the device of FIG. 8 after dopant activation and consequent diffusion.

FIG. 10 is a flow chart illustrating a process for fabricating CMOS circuits in accordance with another embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The preferred embodiments of the present invention are described in a DRAM environment. While the circuit design of these preferred embodiments may be incorporated into any integrated circuit that includes CMOS, such as processors, specialty chips or volatile or non-volatile memory devices, such as DRAM, SRAM, and flash memory, they have particular utility in the integrated circuit memory device context. Of course, larger circuits, computers, devices and systems incorporating the integrated circuits described herein are also contemplated.

A process for fabricating one CMOS region, in a memory device and particularly in DRAM according to one embodiment of the present invention, is illustrated in FIG. 1, and described in greater detail below. FIG. 1 shows a flow chart illustrating one preferred process for fabricating a CMOS region. The steps illustrated in this flow chart are preferably performed in the illustrated order; however, as will be understood by those skilled in the art, they may also be performed in other sequences and various substitutions and replacements may be made. In the discussion below, some of the possible substitutions and replacements will be discussed in further detail. The description below simultaneously makes reference to the process flow of FIG. 1 and the structures shown in FIGS. 2-8.

A substrate is first provided 100 (FIG. 1). The provided substrate 11 is illustrated in FIG. 2 after some initial processing (steps 100-108 of FIG. 1). FIG. 2 shows a cross-sectional view of a portion of the periphery of a memory device 10, wherein the logic of the memory device is generally located. This graphical layout illustrates one pMOS active area and one nMOS active area of logic in the periphery. It will be understood that the integrated circuit includes many such pMOS and nMOS active areas, simultaneously processed on a wafer that will later be diced into chips or dies. Of course, many of these components would be indistinguishable in a purely visual representation, and some of the components shown in FIG. 2 and subsequent figures are artificially distinguished from other materials in order to highlight their functionality. The memory device 10 is preferably built on and in the substrate 11, which forms the lowest level of semiconductor material in which electrical devices are formed. The substrate 11 typically comprises silicon, e.g., epitaxial silicon or the upper surface of a silicon wafer. Of course, other suitable materials (e.g., other group III-V elements) may also be used, as is well-known to those skilled in the art.

In one embodiment, active areas may then be defined 102 (FIG. 1) in the substrate 11 by field isolation, in the form of shallow trench isolation (STI) in the illustrated embodiment. Preferably, the active areas in both the array and periphery are defined by STI. Typically, a hard mask material (e.g., silicon nitride) is first laid down over the substrate 11, and a photoresist layer is deposited over the hard mask. Standard photolithographic techniques may then be used to form a pattern of trenches through the photoresist layer, and the hard mask layer may then be anisotropically etched through the patterned photoresist to obtain a plurality of trenches through these top two layers. The photoresist layer may then be removed by conventional techniques, such as by using an oxygen-based plasma. The trenches may then be extended by a selective etch that removes the exposed silicon forming the substrate 11, thereby forming trenches within the memory device 10. These trenches are then filled with an insulator, such as an oxide. The insulator may be blanket deposited over the entire memory device 10, and then the device may be planarized by any of a number of methods, including, for example, chemical-mechanical polishing (“CMP”) stopping on the hard mask. The resulting isolation trenches 12 may be seen in FIG. 2, separating the n-channel regions 13 a from the p-channel regions 13 b. As will be understood by those skilled in the art, step 102 thereby comprehends the use of a first mask (not shown) to define the active areas.

As shown in FIG. 2, a thin gate dielectric layer 14 may then be formed 103 (FIG. 1) over the active regions of the memory device 10. This dielectric layer 14 comprises silicon oxide in a preferred embodiment, although other dielectric materials (e.g., high k layers such as Ta₂O₅, HfO₂ or ZrO₂) may be used. In one embodiment, the dielectric layer 14 is formed by thermal oxidation of the exposed silicon substrate 11.

In a preferred embodiment, the nMOS and pMOS regions in the periphery may then be doped, defining the transistor wells within these regions. As will be well understood by those skilled in the art, in the nMOS regions, a p-well is formed by doping 104 (FIG. 1) the silicon substrate 11 in that region to form a relatively lightly doped p-type semiconductor. In one preferred embodiment, the nMOS regions are doped with boron. Meanwhile, the pMOS regions are doped to form an n-type semiconductor or n-wells. In a preferred embodiment, the pMOS regions are doped with phosphorous. In one preferred process implementation, each of these steps uses one mask, and so two more masks (not shown) are used in step 104 to define the wells. The process of masking may be performed in a number of ways but is preferably performed as described above, using a photoresist layer patterned according to conventional photolithographic techniques. This lithographic pattern can optionally be transferred to a hard mask to expose the surface of the device 10, thereby opening selected areas of the device 10 for further processing steps, such that the wells may be doped through the masks. After each masking step, the photoresist and any hard mask layers are preferably removed. In addition to doping the wells, these masks can be used for channel enhancement and polysilicon workfunction implants.

In another embodiment, (see FIG. 10 and related description below) the second and third masks can be omitted and well implants can instead be performed at the same time as other doping steps using the fifth and sixth masks (which become the third and fourth masks) described below.

Returning to the embodiment of FIG. 1, the gates 16 may then be patterned or defined 106 in the periphery using a fourth mask. These gates 16 are formed of a conductive material and initially comprise undoped polysilicon in one preferred embodiment. Preferably the gates in the array (not shown) of the memory device 10 are patterned at a subsequent processing step. In further detail, polysilicon may first be blanket deposited over at least the periphery. Then, by a series of photolithographic steps, the polysilicon may be etched back to the gate dielectric layer 14 except in certain lithographically defined regions, where the polysilicon forms gates 16. Preferably the polysilicon is blanket deposited over periphery and array (not shown) regions, but is patterned at this stage 106 only over the periphery. This is because the CMOS gates for the illustrated process employ a bare, uncovered polysilicon, whereas memory array gates preferably include strapping metal or silicide and protective capping layers. A separate mask is used at a later stage to pattern gates in the memory array regions after optional metal or silicide and cap layer formation. In other embodiments, the gates 16 a, 16 b may be metallic, as will be well understood by those skilled in the art. As will be better understood from the discussion below, the thickness of the polysilicon layer is selected to be greater than or equal to the desired source/drain junction depth.

Preferably, the gates 16 in both nMOS and pMOS regions 13 a, 13 b have the same width. Preferably, the gate length is less than 0.5 μm, and more preferably 0.1 μm. As will be seen below, despite the fact that the gate widths are the same for both nMOS and pMOS regions, the process described herein can produce effectively different channel lengths by modulating the spacer width rather than the gate width. As illustrated, the gates 16 are patterned without any capping layer, such that the polysilicon remains exposed on top.

Disposable spacers 18 (FIG. 2) are then formed 108 (FIG. 1) along the vertical surfaces of the gates 16. First, a conformal layer of spacer material is deposited to cover the top surface of the memory device 10. Preferably, the spacer material can be selectively etched with respect to the substrate 11 and the insulator layer 14, and the substrate 11 and the insulator layer 14 can each be selectively etched with respect to the spacer material. In the illustrated embodiment, the spacer material comprises a relatively low density material, such as a TEOS oxide, such that it can be readily stripped (selectively) at a later stage. Of course, in other embodiments, the spacer material may comprise other well-known spacer materials, such as silicon nitride; however, such materials are less desirable for the disposable spacer function. The spacer material may be deposited using any suitable deposition process, such as, for example, chemical vapor deposition (CVD) or physical vapor deposition (PVD).

After laying the spacer material over the vertical and horizontal surfaces of the memory device 10, an anisotropic etch is used to preferentially remove the spacer material from the horizontal surfaces in a directional spacer etch. Thus, the spacer material is formed into the disposable spacers 18, i.e., material extending from the sidewalls of another material. As shown in FIG. 2, the spacers 18 are formed along the vertical surfaces of the CMOS gates 16. In a preferred embodiment, the width of the spacers 18 to which they are initially etched back is approximately the same for what will become both the nMOS and pMOS gates. Thus, no masking step is employed at this stage and the spacers 18 are initially uniformly thick in nMOS and pMOS regions.

In one embodiment, a fifth mask is then used to cover 110 (FIG. 1) the pMOS, while exposing the nMOS regions for subsequent processing. This mask 20 is illustrated in FIG. 3. Optionally, the spacers 18 a surrounding the nMOS gates 16 a may then be partially etched back or trimmed 112 (FIG. 1), narrowing their width W_(S) as illustrated in FIG. 3. As is well understood by those of skill in the art, the spacers for n-channel gates 16 a are preferably smaller than those for p-channel gates 16 b because p-channel should be separated from their respective sources and drains by a greater distance, since n-channel implants are less prone to diffusion. The p-channel has an effective channel length that is defined by the width of the gate 16 b plus approximately two times the width of the spacers 18 b. The n-channel length L_(C) is more narrow, since it is defined in the illustrated embodiment by an identical gate width plus two times the width of the spacers 18 a, which are trimmed relative to spacers 18 b. Thus the p-channel is preferably between more than 10% greater than the n-channel length. More preferably, the effective p-channel length is 10-30% and most preferably 15-20% longer than the n-channel.

For example, in one embodiment, the effective channel length under the p-channel gate 16 b may be between 600 Å and 800 Å, while the effective channel length under the n-channel gate 16 a may be between 400 Å and 800 Å. In such an embodiment, the width of the spacers W_(S), as initially formed, should preferably be sufficient to generate an effective channel length of the nMOS and pMOS gates 16 of at least 800 Å. In a subsequent processing step, the spacers 18 a surrounding the n-channel gates 16 a may be etched back to achieve the desired effective channel length of the n-channel. This etch back may be performed by any of a number of conventional methods.

At step 114 (FIG. 1), once the spacers 18 a and n-channel gate 16 a form an appropriate effective channel length, the source and drain regions 22 a are implanted using the same mask 20, as shown in FIG. 3. As is known in the art, the source and drain regions in the nMOS will preferably be doped (e.g., with phosphorous) to form an n-type semiconducting region in the p-well. In another embodiment, other elements may be used to dope the substrate 11 in order to form an n-type semiconductor.

In the preferred embodiment, because of the location of the spacers 18 a along the sides of the n-channel gate 16 a, the source and drain regions 22 a may be created a distance W_(S) away from the n-channel gate 16 a.

The same doping step 114 (FIG. 1) dopes the illustrated exposed nMOS gates 16 a during this stage of CMOS processing, thus setting the workfunction and differentiating the nMOS gates 16 a from the pMOS gates 16 b. Thus, with the spacers 18 and mask 20 in place, the entire exposed (unmasked) surface of the periphery of the device 10 may be doped with an n-type semiconductor dopant, thereby defining the nMOS gates 16 a, sources and drains 22 a in one step. The lack of a capping layer on the gates 16 a facilitates this simultaneous doping of the gate 16 a with the source/drain regions 22 a. As noted above, the thickness of the polysilicon layer as deposited is selected to be greater than or equal to the desired junction depth, such that the doping 114 does not penetrate into the channel region, but rather remains within the gate above the gate dielectric. In another embodiment (not shown), the gate can include a barrier layer above the gate dielectric to prevent diffusion or implantation of the gate from reaching the underlying channel.

With the same mask 20 in place, the n-channel may also be enhanced during this stage of CMOS processing, step 116. The n-channel is enhanced with p-type doping, (e.g., boron). This enhancement doping is also commonly called a Taylor implant, and need not be performed for some applications. This step, while performed in the illustrated embodiment with the trimmed spacers 18 a along the gates 16 a, may instead be performed with the spacers 18 in place, or after complete removal of the spacers 18/18 a.

With the same mask 20 in place, after completion of the above steps (or before, as discussed above), the spacers 18 a adjacent the walls of the n-channel gates 16 a are preferably removed 118 (FIG. 1), as shown in FIG. 4. In a preferred embodiment, this removal may be performed by a buffered oxide etch or dip, preferentially removing TEOS without harm to the mask or other exposed structures. Choice of the spacer material relative to surrounding materials facilitates the removal. By this removal, access is achieved to those portions of the substrate 11 previously covered by the width, W_(S), of the spacers 18 a. Exposed gate oxide may also be removed, though the gate dielectric 14 remains protected under the nMOS gates 16 a and under the mask 20.

After removal of the disposable spacers 18 a, and with the same mask 20 in place, various doping steps may then be performed in the region between the n-channel gate 16 a and its source and drain regions 22 a in supplemental doping steps 120 (FIG. 1), which can also be referred to as source/drain extension or transistor tailoring implants. With reference to FIG. 5, in one embodiment, as will be well understood in the art, a lightly doped drain (LDD) 23 a may be implanted between these structures, on either side of the n-channel gate 16 a. As illustrated in the schematic cross-section of FIG. 5, the LDD 23 a preferably abuts the source and drain regions 22 a and extends substantially adjacent a top surface of the substrate 11. In a preferred embodiment, a Halo implant 25 a, or pocket implant, may also be implanted substantially underneath the LDD 23 a and the n-channel gate 16 a, as illustrated in FIG. 5. The Halo implant 25 a is formed on either side of the gate 16 a and is more deeply submerged within the substrate 11.

The LDD 23 a and Halo implants 25 a may be provided over the entire exposed surface of the periphery of the memory device 10, but, since these implants are created using much lower doping levels than those used to form the transistor elements, they are “washed out” by the higher doping of previously doped regions, and thus do not change the semiconductor characteristics of these elements.

In another preferred embodiment, the spacers 18 a may not be completely removed in a single step, as disclosed in step 118. Instead, the spacers 18 a may be removed in multiple steps. This preferred embodiment enables a grading of the LDD implants 23 a, with lower levels of doping in later steps, as the regions closer to the n-channel gates 16 a are revealed. In other words, a first portion of the spacers 18 a may be removed, and a first level of doping may be used to form the LDD implant 23 a. A second portion of the spacers 18 a may then be removed, and a second level of doping may be used to form the LDD implant 23 a. Preferably, this second level of doping is at a lower level than the first level of doping, such that the doping trails off as the LDD implant 23 a approaches the gate 16 a. This process may be iterated until the spacers 18 a are entirely removed, or until the LDD implant 23 a is completely defined. This may improve the overall performance of the device 10.

Thus, source/drain, enhancement and supplemental (e.g., LDD and Halo) doping for the nMOS regions are all performed using a single mask due to employment of disposable spacers. This is indicated in FIG. 1 by the dotted box 140.

In step 122 (FIG. 1), the pMOS mask 20 is then removed, and a new, nMOS mask 24 (FIG. 6) created, opening access to the pMOS regions 13 b of the periphery. This is the sixth mask used in the process described herein. The remaining steps disclosed in FIG. 1 (steps 124-132) are illustrated generally in FIGS. 6 and 7. As illustrated, these steps are very similar to steps 112-120, discussed above. The major differences are as follows. First, the dopant types are opposite. For example, instead of using dopants to create n-type source/drain regions, p-type semiconductor doping is performed, preferably using boron. Second, as discussed above, the partial etch back or trim of the spacers 18 b over the p-channel gates 16 b (step 124) will preferably be eliminated or reduced, relative to the pull back described above with respect to the n-channel gates 16 a. In one particular embodiment, the spacers 18 (FIG. 1) may initially be deposited to match the desired effective channel length for the p-channel gates 16 b, and a spacer trim need only be performed on the n-channel gates 16 a. In another embodiment, the spacers 18 b surrounding the p-channel gates 16 b will simply be trimmed less than the spacers 18 a surrounding the n-channel gates 16 a, thereby creating an effective channel length differential between the pMOS and nMOS regions of the device 10.

Thus, gate, source/drain, enhancement and supplemental (e.g., LDD and Halo) doping for the pMOS regions are all performed using a single mask due to employment of disposable spacers. This is indicated in FIG. 1 by the dotted box 150.

In FIG. 8, it may be seen that, after the processing of the respective pMOS and nMOS regions has been completed and after removal of the nMOS mask 24, traditional processing steps may be performed. In one embodiment, new spacers may be formed, around the various circuit elements in the periphery in order to facilitate the formation of self-aligned contacts. Because of the sequence employed, the spacers can be oxide rather than traditional silicon nitride spacers, which exhibit high parasitic capacitance due to higher permittivity and also introduce stress.

More preferably, as illustrated, spacers can be omitted in the final product. Instead, as shown, a low k gap fill oxide 26, with a permittivity preferably less than about 3.5 and more preferably less than about 3.2, is deposited along the top of the memory device 10 directly over conductive sidewalls of the gates 16. Preferably the gates 16 comprise silicon, but it is also contemplated that the gates may be formed of other materials or may have a thin conductive coating.

With reference now to FIG. 9, thereafter the device 10 may undergo annealing (e.g., rapid thermal processing) for dopant activation. This is preferably conducted after forming the gap-fill oxide 26 and can serve to simultaneously densify the oxide 26. As illustrated, dopant activation also drives the dopants from their original locations. In FIG. 9, the original implanted locations of FIG. 5 are illustrated by dotted lines, and the post-activation positions are indicated by solid lines. It will be understood that the pMOS transistors likewise experience the same activation/dopant diffusion during the anneal. The transistors and other circuit elements of the periphery are thereby defined, and lines may be connected thereto according to other steps well known to those of skill in the art. At this or at earlier stages of wafer processing, the array of the memory device 10 may be defined according to various conventional techniques.

Referring again to FIG. 8, the resultant CMOS circuit can have one or more of the following distinguishing features. While the CMOS gates 16 a, 16 b of the illustrated embodiment have the same width, the channel defined between source and drain regions 22 a, 22 b are different, with the p-channel being longer than the n-channel, preferably more than 10% longer, particularly 10-30% and more particularly 15-20% longer on the pMOS side as compared to the nMOS side. A low k gap-fill material directly contacts gate sidewalls, reducing gate-to-drain Miller capacitance. Furthermore, despite the lack of spacers in the illustrated final product, distinct LDD regions are initially formed between source/drain regions and the gate corners (rather than under the gate corners), and later dopant activation (see FIG. 9) cause the LDD to diffuse to the desired location under the gate corners. The resultant device accordingly has a longer life expectancy than LDD formations exclusively formed under the gate.

As is evident from the steps described above, the mask count for the preferred process is less than that for conventional CMOS processing, thereby simplifying the process. In particular, six masks are employed in the above-described preferred embodiment for the definition of the CMOS in the periphery. Gate, source/drain and LDD/Halo doping can be performed at the same stage with one mask for each of the nMOS and pMOS regions, rather than two for each region, thus saving two masks. In exchange, one mask is lost by using separate masks to pattern the transistor gates in the periphery and in the memory arrays.

With reference now to FIG. 10, the well implants can also be performed with the same masks, thus saving another two masks. Thus, from STI definition through completion of CMOS transistor definition in the periphery, the process of FIG. 1 employs six (6) masks, while the process of FIG. 9 employs four (4) masks. In FIG. 10, similar steps to those of FIG. 1 are referenced by similar numbers in the 200 range, rather than the 100 range.

As will be appreciated by a comparison of FIG. 1 with FIG. 10, the processes are very similar, except that the well doping steps 204 a, 204 b are now performed using the same masks used for gate, source/drain, enhancement and supplemental (LDD and Halo) doping. Traditionally, doping of the wells is conducted early in the fabrication process, such that subsequent heat steps can be used to help drive dopants to their ultimately desired depth. However, two factors have recently facilitated doping the wells with the same masks used for source/drain and other doping. The junction depths have become more shallow, and the background doping level (indeed, all doping levels) have increased relatively. Thus, with higher background (well) doping levels, greater crystal faults can be tolerated. Accordingly, state-of-the-art transistor standards enable joinder of well doping with the remaining doping steps for the transistors. Thus, a single mask can be employed for all transistor doping steps for nMOS (see box 240 in FIG. 10) and a single mask for all transistor doping steps for pMOS (see box 250 in FIG. 10).

Significantly, the spacers in place during source/drain doping, which define channel length, can be tailored for nMOS versus pMOS regions without additional masks.

In addition, the manufacturing efficiency for the above process is improved over conventional techniques because higher dose implants may be used. The performance of the CMOS devices may also be improved, with increased mobility and decreased body-effect, or reduced doping can attain the same device performance, as a result of postponing the enhancement and Halo implants until near the end of the process flow, such that reduced dopant diffusion occurs. The gate-to-drain Miller capacitance is also preferably lowered (resulting in faster circuits) because a densified high k dielectric, such as silicon nitride, need not be used for a spacer. Instead an oxide can be used as a spacer, or only the planarized oxide 26 can insulate, as illustrated. Because logic regions of memory devices are not as crowded as the array regions, contacts formed to source and drain regions need not be self-aligned; rather, the contacts vias can be opened in the planarized oxide 26 in a manner spaced from the conductive gate sidewalls, such that only the low k, gap-fill oxide 26 intervenes between the contact and the sidewalls of the gates 16 a, 16 b.

Of course, the devices may also be made more reliable because of the independent spacer tailoring, and thus tailoring the location of doping, in pMOS versus nMOS devices. The process flow also facilitates subsequent siliciding (or silicidation) of the top of the CMOS gates, indeed all along the silicon line that forms the gates, without opening contacts through cap layers. Silicidation of the source and drain regions of these transistors is also facilitated.

While certain embodiments of the inventions have been described, these embodiments have been presented by way of example only, and are not intended to limit the scope of the invention. Indeed, the novel process for forming the CMOS may be modified a great deal, may have various omissions, substitutions and changes, and many of the steps may be performed in a different order without departing from the spirit of the invention. The accompanying claims and their equivalents are intended to cover such forms or modifications as would fall within the scope and spirit of the invention. 

1. A process for forming a memory device, the process comprising: patterning gates in nMOS and pMOS regions for CMOS circuits; forming first disposable spacers surrounding the gates in the nMOS regions and second disposable spacers surrounding the gates in the pMOS regions, wherein the first disposable spacers are smaller than the second disposable spacers; masking the pMOS regions with a first mask; conducting source/drain doping with the first disposable spacers surrounding the gates in the nMOS regions; removing the first disposable spacers and subsequently conducting supplemental doping between source/drain regions and the gates in the nMOS regions while the pMOS regions remain masked with the first mask; masking the nMOS regions with a second mask; conducting source/drain doping with the second disposable spacers surrounding the gates in the pMOS regions; and removing the second disposable spacers and subsequently conducting supplemental doping between source drain regions and the gates in the pMOS regions while the nMOS regions remain masked with the second mask; wherein the gates have a thickness greater than or equal to a source/drain junction depth.
 2. A method of manufacturing a memory device, the method comprising: providing a substrate; defining at least two active areas within the substrate, at least one of said active areas comprising an nMOS region, and at least another of said active areas comprising a pMOS region; patterning a first gate within the nMOS region and a second gate within the pMOS region; simultaneously forming first disposable spacers on the first gate and second disposable spacers on the second gate; masking the pMOS region with a first mask; and while the pMOS region is masked, partially trimming the first disposable spacers to be smaller than a width of the second disposable spacers, doping source/drain regions adjacent the first gate after partially trimming the first disposable spacers, further trimming the first disposable spacers after doping the source/drain regions, and conducting supplemental doping between the source/drain regions of the nMOS region and the first gate after further trimming the first disposable spacers.
 3. The method of claim 2, wherein patterning the first gate and the second gate comprises blanket depositing a gate material in the nMOS and pMOS regions and in a memory array region, and masking the gate material in the memory array region while etching the first and second gates.
 4. The method of claim 2, wherein doping source/drain regions adjacent the first gate further comprises simultaneously doping the first gate.
 5. The method of claim 2, wherein partially trimming comprises defining an effective p-channel length of the second gate and the second disposable spacer that is more than about 10% greater than an effective n-channel length of the first gate and the first disposable spacer.
 6. The method of claim 2, further comprising: masking the nMOS region with a second mask at a different time from masking the pMOS region.
 7. The method of claim 2, further comprising enhancing an n-channel under the first gate.
 8. The method of claim 2, further comprising masking the nMOS region with a second mask and, while the nMOS region is masked, doping source/drain regions adjacent the second gate, doping the second gate, enhancing a p-channel under the second gate, and conducting supplemental doping between the source/drain regions of the pMOS region and the second gate.
 9. The method of claim 5, wherein the effective p-channel length is between about 15% and 20% greater than the effective n-channel length.
 10. The method of claim 7, further comprising doping a transistor well for the nMOS region while the pMOS region is masked with the first mask.
 11. The method of claim 8, further comprising doping a transistor well for the pMOS region while the nMOS region is masked with the second mask.
 12. The method of claim 8, wherein: further trimming comprises removing the first disposable spacers from the first gate after doping the source/drain regions adjacent the first gate and prior to conducting supplemental doping; and further comprising removing the second disposable spacers from the second gate after doping source/drain regions adjacent the second gate and prior to conducting supplemental doping between the source/drain regions of the pMOS region and the second gate.
 13. The method of claim 8, wherein supplemental doping comprises lightly doped drain (LDD) and Halo implants.
 14. A method of fabricating a CMOS circuit that includes an nMOS transistor and a pMOS transistor, the method comprising (a) defining field isolation, (b) patterning nMOS and pMOS gates and (c) conducting transistor doping, wherein (a), (b) and (c) are conducted using six or fewer masks, and wherein (c) comprises: complete doping of the nMOS transistor while the pMOS transistor is masked with a single mask, including: implanting source and drain regions while disposable spacers surround the nMOS gates, performing gate doping on the nMOS gates, performing enhancement doping of the n-channel, and removing the spacers from the nMOS gates and subsequently conducting supplemental doping between the source/drain regions and the nMOS gates, wherein supplemental doping comprises forming a lightly doped drain and a Halo implant, and complete doping of the pMOS transistor while the nMOS transistor is masked with a single mask, including: implanting source and drain regions while disposable spacers surround the pMOS gates, wherein the n-channel width is shorter than the p-channel width, performing gate doping on the pMOS gates, performing enhancement doping of the p-channel, and removing the spacers from the pMOS gates and subsequently conducting supplemental doping between the source/drain regions and the pMOS gates, wherein supplemental doping comprises forming a lightly doped drain and a Halo implant; further comprising partially trimming the spacers on the nMOS gate prior to conducting supplemental doping between doped source/drain regions and the nMOS gate; further comprising further trimming the spacers on the nMOS gate subsequent to partially trimming the spacers on the nMOS gate prior to conducting supplemental doping between doped source/drain regions and the nMOS gate. 